Effect of neutron irradiation on the microstructure of the stainless steel electroslag weld overlay cladding of nuclear reactor pressure vessels

Microstructural changes in the stainless steel weld overlay cladding of reactor pressure vessels subjected to neutron irradiation with a fluence of 7.2×1023nm−2 (E>1MeV) and a flux of 1.1×1017nm−2 s−1 at 290°C were investigated by atom probe tomography. The results showed a difference in the micr...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of nuclear materials 2013-11, Vol.443 (1-3), p.266-273
Hauptverfasser: Takeuchi, T., Kakubo, Y., Matsukawa, Y., Nozawa, Y., Nagai, Y., Nishiyama, Y., Katsuyama, J., Onizawa, K., Suzuki, M.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Microstructural changes in the stainless steel weld overlay cladding of reactor pressure vessels subjected to neutron irradiation with a fluence of 7.2×1023nm−2 (E>1MeV) and a flux of 1.1×1017nm−2 s−1 at 290°C were investigated by atom probe tomography. The results showed a difference in the microstructural changes that result from neutron irradiation and thermal aging. Neutron irradiation resulted in the slight progression of Cr spinodal decomposition and an increase in the fluctuation of the Si, Ni, and Mn concentrations in the ferrite phases, with formation of γ′-like clusters in the austenite phases. On the other hand, thermal aging resulted in the considerable progression of the Cr spinodal decomposition, formation of G-phases, and a decrease in the Si and an increase in the Ni and Mn concentration fluctuations at the matrix in the ferrite phases, without the microstructural changes in the austenite phases.
ISSN:0022-3115
1873-4820
DOI:10.1016/j.jnucmat.2013.07.035