High reflectance ta-C coatings in the extreme ultraviolet
The extreme ultraviolet (EUV) reflectance of amorphous tetrahedrally coordinated carbon films (ta-C) prepared by filtered cathodic vacuum arc was measured in the 30-188-nm range at near normal incidence. The measured reflectance of films grown with average ion energies in the ~70-140-eV range was si...
Gespeichert in:
Veröffentlicht in: | Optics express 2013-11, Vol.21 (23), p.27537-27549 |
---|---|
Hauptverfasser: | , , , , |
Format: | Artikel |
Sprache: | eng |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The extreme ultraviolet (EUV) reflectance of amorphous tetrahedrally coordinated carbon films (ta-C) prepared by filtered cathodic vacuum arc was measured in the 30-188-nm range at near normal incidence. The measured reflectance of films grown with average ion energies in the ~70-140-eV range was significantly larger than the reflectance of a C film grown with average ion energy of ~20 eV and of C films deposited by sputtering or evaporation. The difference is attributed to a large proportion of sp3 atom bonding in the ta-C film. This high reflectance is obtained for films deposited onto room-temperature substrates. The reflectance of ta-C films is higher than the standard single-layer coating materials in the EUV spectral range below 130 nm. A self-consistent set of optical constants of ta-C films was obtained with the Kramers-Krönig analysis using ellipsometry measurements in the 190-950 nm range and the EUV reflectance measurements. These optical constants allowed calculating the EUV reflectance of ta-C films at grazing incidence for applications such as free electron laser mirrors. |
---|---|
ISSN: | 1094-4087 1094-4087 |
DOI: | 10.1364/oe.21.027537 |