Gas-phase synthesis of core / shell particles on the example of TiO2 nanoparticles with electrically conductive sheath

An advanced process enables synthesis and coating of individual TiO sub(2)-core particles with a shell of transparent conducting oxide (TCO) from the gas phase in one reactor. TiO sub(2) particles were coated with fluorine-doped tin oxide (SnO sub(2):F) or antimony-doped tin oxide (SnO sub(2):Sb). Specific electrical conductivity of the core/shell particles was up to 8.10 super(-3) Scm super(-1). Variation of process parameters allows modifying dopant level and conductivity in an easy way.Original Abstract: Ein neuartiges Verfahren zur Herstellung von Kern/Mantel-Partikeln aus der Gasphase ermoglicht die Synthese und Ummantelung eines TiO sub(2)-Partikelkerns mit einer elektrisch leitfaehigen Huelle eines transparenten Oxids in einem Reaktor. Die Ummantelung der TiO sub(2)-Partikel erfolgte mit fluordotiertem (SnO sub(2):F) und antimondotiertem Zinn(IV)-oxid (SnO sub(2):Sb). Die Kern/Mantel-Partikel wiesen eine spezifische Leitfaehigkeit von bis zu 8.10 super(-3) Scm super(-1) auf. Durch Variation von Prozessparametern konnen Dotierungsgrad und die elektrische Leitfaehigkeit der Mantelschichten auf einfache Weise modifiziert werden.