Synthesis and Swelling Behaviors of P(AMPS-co-AAc) Superabsorbent Hydrogel Produced by Glow-Discharge Electrolysis Plasma

Highly swelling P(2-acrylamido-2-methyl-1-propanesulfonic acid- co -acrylic acid) (P(AMPS- co -AAc)) superabsorbent hydrogel was synthesized in aqueous solution by a simple one-step using glow-discharge electrolysis plasma technique, in which N,N’-methylenebisacrylamide was used as a crosslinking agent. The structure, thermal stability and morphology of P(AMPS- co -AAc) superabsorbent hydrogel were characterized by Fourier transform infrared spectroscopy, thermogravimetric analysis, and scanning electron microscopy. A mechanism for synthesis of P(AMPS- co -AAc) superabsorbent hydrogel was proposed. The reaction parameters affecting the equilibrium swelling (i.e., discharge voltage, discharge time, macroscopic temperature of the liquid phase, mass ratio of AMPS to AAc, and content of crosslinker) were systematically optimized to achieve a superabsorbent hydrogel with a maximum swelling capacity. The hydrogel formed which absorbed about 1,685 g H 2 O/g dry hydrogel of the optimized product was used to study the influence of various pH values and salts solutions (NaCl, KCl, MgCl 2 , and CaCl 2 ) on the equilibrium swelling. In addition, swelling kinetics in distilled water and on–off switching behavior were preliminarily investigated. The results showed that superabsorbent hydrogel was responsive to the pH and salts.