Influence of Boron-Containing Dopants on Superconducting Properties of (Bi, Pb)-2223 HTS

The influence of addition of lead borate Pb(BO 2 ) 2 and boron oxide B 2 O 3 on the phase evolution and superconducting properties of (Bi, Pb)-2223 HTSs synthesized by the solid-state reaction method in alumina crucibles has been studied. X-ray diffraction, resistivity, critical current density, and AC susceptibility measurements were performed on the prepared compounds. Obtained results have shown that boron-containing dopants lead to the drastic enhancement of the (Bi, Pb)-2223 phase formation. Boron-doped samples reveal a significant increase in both the zero resistivity temperature and transport critical current density compared to the undoped specimen. On the other hand, a high content of boron-containing dopants causes the appearance of a very low- T c 2201 phase and leads to a deterioration of coupling between superconducting grain boundaries. Obtained results could enable us to develop a cheap and energy efficient fabrication technology for nearly single (Bi, Pb)-2223 phase superconducting materials via heat treatment of boron-incorporated precursors in an alumina crucibles.