Improved efficiency of dye-sensitized solar cells by design of a proper double layer photoanode electrodes composed of Cr-doped TiO2 transparent and light scattering layers

A new strategy for enhancing the efficiency of TiO 2 dye-sensitized solar cells (DSSCs) by design of a new double layer film doped with Cr ions, with various morphologies, is reported. X-ray diffraction and field emission scanning electron microscope (FE-SEM) analyses revealed that the synthesized nanoparticles had uniform and nanometer grains with different phase compositions and average crystallite size in the range of 10–12 nm depending upon Cr atomic percentage. UV–vis absorption showed that Cr introduction enhanced the visible light absorption of TiO 2 nanoparticles by shifting the absorption onset to visible light region. Furthermore, the band gap energy of nanoparticles decreased with an increase in dopant concentration due to reduction of particle size. It was found that, 3 at.% Cr-doped TiO 2 DSSC in the form of a double-layer film composed of TiO 2 nanoparticles, as the under-layer, and mixtures of nano- and micro-particles with weight ratio of 80:20, as the over-layer, (i.e., CT3/NM3 solar cell) had the highest power conversion efficiency of 7.02 %, short current density of 17.32 mA/cm 2 and open circuit voltage of 674 mV. This can be related to achievement of a balance among the electron injection, light scattering effect and dye sensitization parameters. Optimization of light scattering effect of photoanode electrode led to improve the photovoltaic performance of CT3/NM3 double-layer solar cell and was demonstrated by diffuse reflectance spectroscopy. The presented strategy would open up new insight into fabrication of low-cost TiO 2 DSSCs with high power conversion efficiency.