THE EQUAL CHANNEL ANGULAR EXTRUSION PROCESS OF MULTIPHASE HIGH STRENGTH ALUMINIUM BRONZE

The aim of the research was to determine the deformation condition of ECAP process of multiphase high strength aluminium bronze BA1032. The studies have indicated that it is possible to deform multiphase aluminium bronze BA1032 in the ECAP process at a temperature of 400 degree C and die angle Phi =110 degree . The deformation of the bronzes at lower temperatures encounters some difficulties - cracks appear which make repeated ECAP impossible. The cracks appear on the top surface of the samples where it contacts the surface of the outlet channel. FEM simulations show that the largest plastic strains occur in this area. The proposed ECAP method of large plastic deformations as applied to the investigated aluminium bronzes makes it possible to obtain very strong refinement especially of eutectoid alpha + gamma sub(2).Original Abstract: Celem pracy bylo okreslenie warunkow odksztalcania w procesie ECAP wysokowytrzymalych wielofazowych brazow aluminiowych. Przeprowadzone badania wskazuja na mozliwosc odksztalcania wielofazowych brazow aluminiowych w tym procesie w temperaturze 400 degree C dla kata matrycy Phi = 110 degree . Pewne trudnosci sprawia odksztalcanie brazu w nizszych temperaturach, gdyz pojawiaja sie wdwczas pekniecia, ktore uniemozliwiaja prowadzenie procesu wielokrotnego przeciskania probek przez kanal katowy. Pekniecia pojawiaja sie na gornej powierzchni probek w miejscu kontaktu z powierzchnia kanalu wyjsciowego. Jak wykazuje symulacje MES w miejscu tym wystepuja najwieksze odksztalcenia plastyczne. Zastosowana metoda duzych odksztalcen plastycznych ECAP w przypadku badanych brazow aluminiowych pozwala uzyskac bardzo silne rozdrobnienie glownie eutektoidu alpha + gamma sub(2).