Characterization of sodium alginate and its block fractions by surface-enhanced Raman spectroscopy
The surface‐enhanced Raman scattering (SERS) of sodium alginates and their hetero‐ and homopolymeric fractions obtained from four seaweeds of the Chilean coast was studied. Alginic acid is a copolymer of β‐D‐mannuronic acid (M) and α‐L guluronic acid (G), linked 1 → 4, forming two homopolymeric frac...
Gespeichert in:
Veröffentlicht in: | Journal of Raman spectroscopy 2010-07, Vol.41 (7), p.758-763 |
---|---|
Hauptverfasser: | , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | The surface‐enhanced Raman scattering (SERS) of sodium alginates and their hetero‐ and homopolymeric fractions obtained from four seaweeds of the Chilean coast was studied. Alginic acid is a copolymer of β‐D‐mannuronic acid (M) and α‐L guluronic acid (G), linked 1 → 4, forming two homopolymeric fractions (MM and GG) and a heteropolymeric fraction (MG). The SERS spectra were registered on silver colloid with the 632.8 nm line of a HeNe laser. The SERS spectra of sodium alginate and the polyguluronate fraction present various carboxylate bands which are probably due to the coexistence of different molecular conformations. SERS allows to differentiate the hetero‐ and homopolymeric fractions of alginic acid by characteristic bands. In the fingerprint region, all the poly‐D‐mannuronate samples present a band around 946 cm−1 assigned to CO stretching, and CCH and COH deformation vibrations, a band at 863 cm−1 assigned to deformation vibration of β‐C1H group, and one at 799–788 cm−1 due to the contributions of various vibration modes. Poly‐L‐guluronate spectra show three characteristic bands, at 928–913 cm−1 assigned to symmetric stretching vibration of COC group, at 890–889 cm−1 due to CCH, skeletal CC, and CO vibrations, and at 797 cm−1 assigned to α C1H deformation vibration. The heteropolymeric fractions present two characteristic bands in the region with the more important one being an intense band at 730 cm−1 due to ring breathing vibration mode. Copyright © 2009 John Wiley & Sons, Ltd.
Surface‐enhanced Raman spectroscopy (SERS) allows to differentiate fractions of sodium alginates by characteristic bands; poly‐D‐mannuronate shows the β glycosidic linkage vibration at 863 cm−1, poly‐L‐guluronate presents a band associated to α glycosidic linkage at 797 cm−1, and the heteropolymeric fraction presents an intense band at 730 cm−1. |
---|---|