Oxidative dissolution of pyrite surfaces by hexavalent chromium: Surface site saturation and surface renewal

In-situ reduction of toxic Cr(VI) to nontoxic Cr(III) represents an important natural attenuation process for Cr(VI)-impacted environments. This study investigates the stoichiometry and kinetics of Cr(VI) reduction by pyrite, a reduced iron–sulfur mineral ubiquitous in recent estuarine and marine sediments. Pyrite suspensions at surface loadings of 0.28–2.10m2/L (typical of estuarine or marine sediments) were capable of completely reducing 7–120μM Cr(VI) on the timescale of minutes to days, with the time to reaction completion decreasing with increasing pyrite loading, decreasing initial Cr(VI) concentration, and decreasing suspension pH. Analysis of metal species (Cr and Fe) and sulfur species in solution and at the mineral surface indicated that Cr(VI) oxidatively dissolved the pyrite surface, releasing ferrous iron and sulfate into solution as the reaction progressed. Surface disulfide groups were postulated as the Cr(VI)-reactive surface entity. Net production or consumption of aqueous Fe(II) was shown to depend upon the relative rates of proton-promoted Fe(II) release, Fe(II) release due to oxidative dissolution of pyrite in the presence of Cr(VI), and Fe(II) consumption due to homogeneous reaction with Cr(VI). Kinetics of Cr(VI) reduction by pyrite displayed a biphasic pattern, and the time to reaction completion increased dramatically with increasing initial Cr(VI) concentration. Rapid Cr(VI) removal occurred early in the reaction progress, attributable to Cr(VI) loss under an adsorption-limited regime. Slow, approximately zero-order, Cr(VI) removal occurred over the bulk of the time courses, and corresponded to Cr(VI) removal under surface site saturation conditions. Stoichiometric Cr(VI) reduction was able to proceed under surface site limited conditions owing to regeneration of reactive surface sites following desorption/dissolution of oxidized surface products, as demonstrated in repeat Cr(VI)-spiking experiments. The role of surface passivation was evaluated by comparing rates of Cr(VI) reduction in the presence and absence of the Cr(III)-complexing agent citrate. While citrate addition significantly enhanced Cr(III) solubility, rates of Cr(VI) reduction were only marginally accelerated, suggesting that Cr(OH)3(s) coatings did not completely block access of Cr(VI) to reactive surface sites on pyrite. Given the rapid rates of Cr(VI) reduction with pyrite under pH and surface coverage conditions typical of natural environments, we propose that Cr