Formation behavior of different topographies of crack growth path under high and low cyclic stresses in ultrafine-grained copper

Fatigue tests of ultrafine-grained copper specimens were conducted. The crack growth direction under constant stress depended on the magnitude of the stress amplitude. It occurred perpendicular to the loading axis at low stresses and was inclined at 45° to the loading axis at high stress. To clarify...