A Viable Route for Dense TiO^sub 2^ with a Low Microwave Dielectric Loss
Dense, high-purity TiO... was prepared from commercially available powders. These powders were deagglomerated, colloidally stabilized in aqueous NH..., followed by screening to remove residual agglomerates. Homogeneous compacts were formed using colloidal-filtration followed by sintering. TiO... wit...
Gespeichert in:
Veröffentlicht in: | Journal of the American Ceramic Society 2010-04, Vol.93 (4), p.969 |
---|---|
Hauptverfasser: | , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Dense, high-purity TiO... was prepared from commercially available powders. These powders were deagglomerated, colloidally stabilized in aqueous NH..., followed by screening to remove residual agglomerates. Homogeneous compacts were formed using colloidal-filtration followed by sintering. TiO... with >99.5% density and 400 MPa flexural strength was obtained at a sintering temperature as low as 1000...C. The dielectric loss of this TiO2 was 1.4 x 10... at 6.4 GHz at room temperature. This implied that the product of the quality factor and frequency, (Qxf )=f/tan ..., was 46 000 GHz, ...7.6 times higher than 6000 GHz (Q |
---|---|
ISSN: | 0002-7820 1551-2916 |