Wood Biodegradation in Laboratory-Scale Landfills

The objective of this research was to characterize the anaerobic biodegradability of major wood products in municipal waste by measuring methane yields, decay rates, the extent of carbohydrate decomposition, carbon storage, and leachate toxicity. Tests were conducted in triplicate 8 L reactors operated to obtain maximum yields. Measured methane yields for red oak, eucalyptus, spruce, radiata pine, plywood (PW), oriented strand board (OSB) from hardwood (HW) and softwood (SW), particleboard (PB) and medium-density fiberboard (MDF) were 32.5, 0, 7.5, 0.5, 6.3, 84.5, 0, 5.6, and 4.6 mL CH4 dry g–1, respectively. The red oak, a HW, exhibited greater decomposition than either SW (spruce and radiata), a trend that was also measured for the OSB-HW relative to OSB-SW. However, the eucalyptus (HW) exhibited toxicity. Thus, wood species have unique methane yields that should be considered in the development of national inventories of methane production and carbon storage. The current assumption of uniform biodegradability is not appropriate. The ammonia release from urea formaldehyde as present in PB and MDF could contribute to ammonia in landfill leachate. Using the extent of carbon conversion measured in this research, 0–19.9%, predicted methane production from a wood mixture using the Intergovernmental Panel for Climate Change waste model is only 7.9% of that predicted using the 50% carbon conversion default.