Single crystal PZN/PT-polymer composites for ultrasound transducer applications

Single crystal relaxor ferroelectrics of PZN-8%PT were investigated for potential application in ultrasound transducers. The full set of electromechanical properties was determined using combined resonance and laser interferometry techniques. Ultra-high length extensional coupling (k/sub 33/) of 0.94 was observed, a 25% increase over Navy Type VI PZT ceramics. The thickness extensional coupling (k/sub t/) of 0.48 was comparable to PZT compositions, and the compliance S/sub 33//sup E/ was a factor of six greater. To maximize height extensional coupling (k'/sub 33/), while minimizing length extensional coupling k/sub 31/ in array elements, it was necessary to align the elements along the crystallographic direction in the x-y plane. Mode coupling plots and test samples for array elements determined that width-to-height ratios of less than 0.5 were desired, similar to the requirement for polycrystalline PZT ceramics. Modeling of 1-3 composites and experimental results demonstrated that thickness coupling greater than 0.80 could be achieved with a 40% to 70% volume fraction of PZN-PT. Although this is a substantial increase over PZT 1-3 composites, with a thickness coupling coefficient of 0.66, it represents a smaller fraction of the length extensional coupling k/sub 33/. This reduction may be a consequence of the increased compliance of PZN-PT, which results in significant clamping by the polymer matrix. Ultrasonic transducers fabricated using PZN-8%PT 1-3 composites achieved experimental bandwidths as high as 141%. The pulse-echo responses displayed good agreement with modeled results using the Redwood equivalent circuit.