Study of corrosion resistance of cold sprayed Al + B4C composite coatings

The work presents the results of the corrosion resistance study of composite coatings obtained by cold spraying of the aluminum and boron carbide powder mixture on the surface of 08Cr18Ni10Ti austenitic steel. Their chemical and phase compositions, macro- and microstructure, as well as the effect of subsequent heat treatment are analyzed. It is shown that the corrosion of coatings in a 2% boric acid solution at 60 °C is accompanied by an increase in the sample mass and the formation of an aluminum oxide layer. The minimum mass change was observed in case of the coating heat treated at 400 °C, while an increase in heat treatment temperature leads to the intensification of corrosion destruction.