Synthesis of α-Bi/SrTiO3 heterostructure through the Eu-induced reduction of Bi2O2Se/SrTiO3

Thin Bi films, especially noncentrosymmetric α-phase Bi films (α-Bi), have attracted considerable attention in recent years due to their intriguing physical properties such as ferroelectricity, nonlinear optical response, and coherent spin transport. However, the current experimental preparation of...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Applied physics letters 2024-06, Vol.124 (26)
Hauptverfasser: Kong, Lingyuan, Zhang, Wei, Fan, Zixin, Ling, Haoming, Ran, Feng, Li, Dingyi, Wang, Zihao, Chen, Pan, Liang, Yan, Zhang, Jiandi
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Thin Bi films, especially noncentrosymmetric α-phase Bi films (α-Bi), have attracted considerable attention in recent years due to their intriguing physical properties such as ferroelectricity, nonlinear optical response, and coherent spin transport. However, the current experimental preparation of α-Bi films still presents substantial challenges, resulting in only isolated α-Bi islands being achieved. In this study, α-Bi/SrTiO3 (α-Bi/STO) was synthesized from a Bi2O2Se/STO (BOS/STO) heterostructure by depositing a Eu layer and reducing a BOS film. The so-formed α-Bi/STO interface features metallic conductivity with electron mobility of 7.7 × 104 cm2/V s and ultralow resistivity of 1 nΩ cm at 2 K, as well as high residual resistance ratios R300 K/R2 K up to 2353. Furthermore, we observed a complex weak antilocalization–weak localization–weak antilocalization crossover with increasing magnetic field at temperatures below 10 K. Our work presents the synthesis of α-Bi films, which could potentially serve as a valuable platform for experimental validation of diverse theoretical predictions associated with α-Bi heterostructures. Furthermore, this special synthesis method provides valuable insights into the preparation of other metastable films.
ISSN:0003-6951
1077-3118
DOI:10.1063/5.0218075