A comparative analysis of flexural strength between 3D printed lattice structures (ABS) compared with and without the silica nanoparticle

This study was carried out to determine the Flexural Strength of (ABS) Acyroonitrile Butadiene Styrene and the Flexural Strength of (ABS) composites with silica nanoparticles. There were 20 specimens for each group of sample that served as an experimental group that had ABS with filler and a control group comprised of ABS without filler. The sample size was decided at the 80% power, at 0.05 alpha per set. The base materials incorporated were Acrylonitrile Butadiene Styrene with the Silica nanoparticles filler added. This is testified by the fact that the Flexural Strength of ABS Composite in contrast with ABS Composite with 2% volume fraction of novel silica nanoparticles filler was higher. The P value was determined as 0.00 (p