Role of Iron-Rich Phases and Porosity on the Ductility of Rheocast Al-Mg-Si-Alloys

Treatment of the slurry is important during RheoMetalTM casting. In this work, semi-solid slurries were prepared under different stirring intensities, using two types of stirrers: a naked rod (for regular stirring) and a rod with two blades (for intensified stir). Tensile tests were performed, investigating fracture surfaces, as well as metallographic samples. The results show that intensified stir produces castings with finer primary particles and a more homogeneous microstructure. On the other hand, more faceted Fe-rich phases are found along the α-Al grains boundary as well, due to the dissolution of Fe from the stirrers. Moreover, for intensified stir castings, the porosity found on the fracture surfaces are smaller, while more brittle eutectic phases and second (intermetallic) phases, especially Fe-rich phases, are observed. Consequently, the castings with intensified stir show worse ductility. Finally, a quantitative analysis was made regarding ductility, affected both by porosity and the presence of Fe-rich phases.