Fine Copper Powders Production

The article is devoted to the description of a method for producing electrolytic copper powder with an average particle size of 3 to 10 μm. In order to increase the proportion of the finely dispersed fraction during the electrolysis process, the composition of the electrolyte was changed. In particu...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Diffusion and defect data. Solid state data. Pt. A, Defect and diffusion forum Defect and diffusion forum, 2021-08, Vol.410, p.418-424
Hauptverfasser: Yakovleva, Lyubov M., Voinkov, Roman S., Timofeev, Konstantin L., Agarova, Natalia E.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The article is devoted to the description of a method for producing electrolytic copper powder with an average particle size of 3 to 10 μm. In order to increase the proportion of the finely dispersed fraction during the electrolysis process, the composition of the electrolyte was changed. In particular, the content of chloride ions was increased from 6 to 53 mg/dm3. After the growth of the powder in industrial baths, its subsequent drying and sieving on vibrating screens, samples were obtained with a fraction of 5 μm content in the range from 3 to 38 %. Additionally, air classification of powders was carried out at various speeds of the classifier rotor from 800 to 2000 rpm. Based on the results of the study, the optimal ranges of the specific surface area and the size of the initial powder particles before classification, as well as the composition of the electrolyte and the operating modes of the classifier, were determined.
ISSN:1012-0386
1662-9507
1662-9507
DOI:10.4028/www.scientific.net/DDF.410.418