Synergistic effect of Ni doping on the dielectric and electrochemical properties of WO3 nanostructures for supercapacitor applications

The present work explores a systematic investigation of the microstructural, optical, and dielectric properties of W 1− x Ni x O 3 ( x  = 0, 0.02, 0.04, and 0.06) samples and their application in supercapacitors. The sol–gel auto-combustion process was used to synthesize these samples, and a number...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials science. Materials in electronics 2024-07, Vol.35 (21), p.1450, Article 1450
Hauptverfasser: Abushad, M., Khan, Rayyan Ubaid, Arshad, M., Nadeem, M., Ahmed, Hilal, Ansari, M. Yusuf, Riyaz, Husain, Shahid, Khan, Wasi
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The present work explores a systematic investigation of the microstructural, optical, and dielectric properties of W 1− x Ni x O 3 ( x  = 0, 0.02, 0.04, and 0.06) samples and their application in supercapacitors. The sol–gel auto-combustion process was used to synthesize these samples, and a number of analytical techniques such as x-ray diffraction (XRD), Fourier Transform Infrared (FTIR) spectroscopy, Raman, Scanning Electron Microscopy (SEM), UV–visible spectroscopy, dielectric measurements, cyclic voltammetry (CV), and electrochemical impedance spectroscopy (EIS) were used to characterize them. The Rietveld refined XRD patterns confirm the monoclinic phase with space group P21/n in a single phase. FTIR spectroscopy confirms the functional groups associated with stretching and bending vibrational modes at various wavenumbers. Raman spectroscopy ensures the phase purity of the materials and shows a blue shift with Ni doping. SEM microscopy reveals a uniform surface morphology as well as particle agglomeration at the surface. UV–visible studies reveal a significant decrease in the bandgap (2.13–1.81 eV) as the Ni concentration is increased. Dielectric studies show that as the frequency rises, the dielectric constant decreases and becomes saturated at higher frequencies. The highest value of the dielectric constant (ε') is observed for the 4% Ni-doped WO 3 sample. The electrochemical and capacitive properties have been characterized and studied using CV and EIS analysis. Cyclic voltammetry tests were carried out in the range of − 0.2 to 0.8 V with varying scan rates (5–100 mVs −1 ), exhibiting a significantly large area under the CV curve, hence higher values of specific capacitance. The maximum specific capacitance at a scan rate of 5 mVs −1 for each sample of W 1− x Ni x O 3 ( x  = 0, 0.02, 0.04, and 0.06) is found to be 126.671, 192.31, 278.52, and 128.58 Fg −1 , respectively, in 2M KOH electrolyte. Thus, the synthesized samples exhibit potential for application as electrode materials for supercapacitors.
ISSN:0957-4522
1573-482X
DOI:10.1007/s10854-024-13112-3