Enhancing Thermal Insulation of Geothermal Well Cement Using Alkali-Activated Straw Ash and Natural Zeolite

To improve the heat extraction efficiency from the wellbore fluids to the stratum in the geothermal well, thermal insulation cement, which is prepared by alkali-excited straw ash-natural zeolite, was based on the orthogonal test. The properties of thermal insulation cement, such as compressive stren...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Coatings (Basel) 2024-04, Vol.14 (4), p.507
Hauptverfasser: Ji, Ying, Sha, Qianqian, Zhu, Gang, Xue, Yuze, Zhang, Tinghui
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:To improve the heat extraction efficiency from the wellbore fluids to the stratum in the geothermal well, thermal insulation cement, which is prepared by alkali-excited straw ash-natural zeolite, was based on the orthogonal test. The properties of thermal insulation cement, such as compressive strength, thermal conductivity and fluidity, were tested, and the comprehensive evaluation and range analysis of thermal insulation cement were carried out by using analytic hierarchy process (AHP) as a macro reference index. The results show that the alkali equivalent of natural zeolite and water glass are the two biggest factors affecting the properties of cement. The compressive strength of the optimal mixture at 38 °C and 60 °C for 8 h is 9.26 MPa and 24.46 MPa, respectively, and the thermal conductivity reduction rates at 30 °C, 60 °C and 90 °C are 42.41%, 50.29% and 54.03%, respectively. The initial consistency of the optimal mixture is 13.9 BC and the consistency time is 123 min, which can be used for engineering cementing. In addition, the thickening time of cement can be adjusted according to water-reducing agent and retarder to meet the actual construction requirements of cementing.
ISSN:2079-6412
2079-6412
DOI:10.3390/coatings14040507