Graphene-Material-Modified PMMA Coated with 1,3,5,7-Tetranitro-1,3,5,7-tetraazacyclooctane

Since the energetic material 1,3,5,7-tetranitro-1,3,5,7-tetraazacyclooctane (HMX) has potential safety hazards during its application, it was chosen to solve this problem by coating the surface of HMX through the self-polymerization reaction of methyl methacrylate (MMA). However, its mechanical prop...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Processes 2023-10, Vol.11 (10), p.2945
Hauptverfasser: Hou, Conghua, Wu, Nan, Zhang, Xin, Li, Zerui, Du, Yuxing, Wang, Jingyu
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Since the energetic material 1,3,5,7-tetranitro-1,3,5,7-tetraazacyclooctane (HMX) has potential safety hazards during its application, it was chosen to solve this problem by coating the surface of HMX through the self-polymerization reaction of methyl methacrylate (MMA). However, its mechanical properties were poor for further application, so graphene oxide (GO), hydroxylated graphene (GO-OH), and reduced graphene oxide (rGO) were chosen to be doped into PMMA for coating modification. The properties were also investigated. The composite microspheres were regular in shape. Furthermore, it was observed that graphene materials were present on the surface of the microspheres, and no crystal transformation of HMX occurred during the process. The thermal stability of the composite microspheres was improved, and the activation energies of the HMX/PMMA/GO, HMX/PMMA/rGO and HMX/PMMA/GO-OH composite microspheres were increased compared with those of the HMX/PMMA microspheres. At the same time, the high-energy dropout characteristics of the composite microspheres were improved, and the impact sensitivity of all microspheres was reduced, compared with that of the HMX/PMMA microspheres. The compressive strength of pillars pressed with composite microspheres increased by 1.91, 0.92 and 3.13 MPa, respectively. The mechanical properties of the composite microspheres were improved. As a result, HMX/PMMA composite microspheres have better properties.
ISSN:2227-9717
2227-9717
DOI:10.3390/pr11102945