Fatigue Failure of Hydraulic Power Equipment during a Long Service Life

Fatigue Failure of Hydraulic Power Equipment during a Long Service Life

The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Steel in translation 2023-03, Vol.53 (3), p.243-247
Hauptverfasser: Rudenko, A. L., Mishakin, V. V., Fomin, A. E., Sergeeva, O. A.
Format: Artikel
Sprache:eng
Schlagworte:
Chemistry and Materials Science
Fatigue failure
Fracture mechanics
Hydraulic turbines
Materials Science
Service life
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
container_end_page 247
container_issue 3
container_start_page 243
container_title Steel in translation
container_volume 53
creator Rudenko, A. L.
Mishakin, V. V.
Fomin, A. E.
Sergeeva, O. A.
description The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of operation and extending the service life of equipment is discussed.
doi_str_mv 10.3103/S0967091223030142
format Article
fullrecord <record><control><sourceid>proquest_cross</sourceid><recordid>TN_cdi_proquest_journals_2828400051</recordid><sourceformat>XML</sourceformat><sourcesystem>PC</sourcesystem><sourcerecordid>2828400051</sourcerecordid><originalsourceid>FETCH-LOGICAL-c1832-47ebb80deaa5d9cdc10d945366da1055d7d1ad87da00bc07e5b2c3446530842a3</originalsourceid><addsrcrecordid>eNp1UMtKw0AUHUTBWv0AdwOuo3deyWQppWmFgEJ1HSYzN2VK26QzjdK_N6GCC3F1FufFOYTcM3gUDMTTCvI0g5xxLkAAk_yCTFguVAK51pdkMtLJyF-Tmxg3ACrlik3IojBHv-6RFsZv-4C0bejy5ILpt97St_YLA50fet_tcH-krg9-v6aGlu0AKwyf3iItfYO35Kox24h3PzglH8X8fbZMytfFy-y5TCzTgicyw7rW4NAY5XLrLAOXSyXS1BkGSrnMMeN05gxAbSFDVXMrpEyVAC25EVPycM7tQnvoMR6rTduH_VBZcc21hGEZG1TsrLKhjTFgU3XB70w4VQyq8a_qz1-Dh589sRtHYvhN_t_0DSwGasM</addsrcrecordid><sourcetype>Aggregation Database</sourcetype><iscdi>true</iscdi><recordtype>article</recordtype><pqid>2828400051</pqid></control><display><type>article</type><title>Fatigue Failure of Hydraulic Power Equipment during a Long Service Life</title><source>SpringerLink Journals - AutoHoldings</source><creator>Rudenko, A. L. ; Mishakin, V. V. ; Fomin, A. E. ; Sergeeva, O. A.</creator><creatorcontrib>Rudenko, A. L. ; Mishakin, V. V. ; Fomin, A. E. ; Sergeeva, O. A.</creatorcontrib><description>The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of operation and extending the service life of equipment is discussed.</description><identifier>ISSN: 0967-0912</identifier><identifier>EISSN: 1935-0988</identifier><identifier>DOI: 10.3103/S0967091223030142</identifier><language>eng</language><publisher>Moscow: Pleiades Publishing</publisher><subject>Chemistry and Materials Science ; Fatigue failure ; Fracture mechanics ; Hydraulic turbines ; Materials Science ; Service life</subject><ispartof>Steel in translation, 2023-03, Vol.53 (3), p.243-247</ispartof><rights>Allerton Press, Inc. 2023. ISSN 0967-0912, Steel in Translation, 2023, Vol. 53, No. 3, pp. 243–247. © Allerton Press, Inc., 2023. Russian Text © The Author(s), 2021, published in Remont. Vosstanovlenie. Modernizatsiya, 2021, No. 9, pp. 18–24.</rights><lds50>peer_reviewed</lds50><woscitedreferencessubscribed>false</woscitedreferencessubscribed><cites>FETCH-LOGICAL-c1832-47ebb80deaa5d9cdc10d945366da1055d7d1ad87da00bc07e5b2c3446530842a3</cites></display><links><openurl>$$Topenurl_article</openurl><openurlfulltext>$$Topenurlfull_article</openurlfulltext><thumbnail>$$Tsyndetics_thumb_exl</thumbnail><linktopdf>$$Uhttps://link.springer.com/content/pdf/10.3103/S0967091223030142$$EPDF$$P50$$Gspringer$$H</linktopdf><linktohtml>$$Uhttps://link.springer.com/10.3103/S0967091223030142$$EHTML$$P50$$Gspringer$$H</linktohtml><link.rule.ids>314,776,780,27901,27902,41464,42533,51294</link.rule.ids></links><search><creatorcontrib>Rudenko, A. L.</creatorcontrib><creatorcontrib>Mishakin, V. V.</creatorcontrib><creatorcontrib>Fomin, A. E.</creatorcontrib><creatorcontrib>Sergeeva, O. A.</creatorcontrib><title>Fatigue Failure of Hydraulic Power Equipment during a Long Service Life</title><title>Steel in translation</title><addtitle>Steel Transl</addtitle><description>The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of operation and extending the service life of equipment is discussed.</description><subject>Chemistry and Materials Science</subject><subject>Fatigue failure</subject><subject>Fracture mechanics</subject><subject>Hydraulic turbines</subject><subject>Materials Science</subject><subject>Service life</subject><issn>0967-0912</issn><issn>1935-0988</issn><fulltext>true</fulltext><rsrctype>article</rsrctype><creationdate>2023</creationdate><recordtype>article</recordtype><recordid>eNp1UMtKw0AUHUTBWv0AdwOuo3deyWQppWmFgEJ1HSYzN2VK26QzjdK_N6GCC3F1FufFOYTcM3gUDMTTCvI0g5xxLkAAk_yCTFguVAK51pdkMtLJyF-Tmxg3ACrlik3IojBHv-6RFsZv-4C0bejy5ILpt97St_YLA50fet_tcH-krg9-v6aGlu0AKwyf3iItfYO35Kox24h3PzglH8X8fbZMytfFy-y5TCzTgicyw7rW4NAY5XLrLAOXSyXS1BkGSrnMMeN05gxAbSFDVXMrpEyVAC25EVPycM7tQnvoMR6rTduH_VBZcc21hGEZG1TsrLKhjTFgU3XB70w4VQyq8a_qz1-Dh589sRtHYvhN_t_0DSwGasM</recordid><startdate>20230301</startdate><enddate>20230301</enddate><creator>Rudenko, A. L.</creator><creator>Mishakin, V. V.</creator><creator>Fomin, A. E.</creator><creator>Sergeeva, O. A.</creator><general>Pleiades Publishing</general><general>Springer Nature B.V</general><scope>AAYXX</scope><scope>CITATION</scope><scope>8BQ</scope><scope>8FD</scope><scope>JG9</scope></search><sort><creationdate>20230301</creationdate><title>Fatigue Failure of Hydraulic Power Equipment during a Long Service Life</title><author>Rudenko, A. L. ; Mishakin, V. V. ; Fomin, A. E. ; Sergeeva, O. A.</author></sort><facets><frbrtype>5</frbrtype><frbrgroupid>cdi_FETCH-LOGICAL-c1832-47ebb80deaa5d9cdc10d945366da1055d7d1ad87da00bc07e5b2c3446530842a3</frbrgroupid><rsrctype>articles</rsrctype><prefilter>articles</prefilter><language>eng</language><creationdate>2023</creationdate><topic>Chemistry and Materials Science</topic><topic>Fatigue failure</topic><topic>Fracture mechanics</topic><topic>Hydraulic turbines</topic><topic>Materials Science</topic><topic>Service life</topic><toplevel>peer_reviewed</toplevel><toplevel>online_resources</toplevel><creatorcontrib>Rudenko, A. L.</creatorcontrib><creatorcontrib>Mishakin, V. V.</creatorcontrib><creatorcontrib>Fomin, A. E.</creatorcontrib><creatorcontrib>Sergeeva, O. A.</creatorcontrib><collection>CrossRef</collection><collection>METADEX</collection><collection>Technology Research Database</collection><collection>Materials Research Database</collection><jtitle>Steel in translation</jtitle></facets><delivery><delcategory>Remote Search Resource</delcategory><fulltext>fulltext</fulltext></delivery><addata><au>Rudenko, A. L.</au><au>Mishakin, V. V.</au><au>Fomin, A. E.</au><au>Sergeeva, O. A.</au><format>journal</format><genre>article</genre><ristype>JOUR</ristype><atitle>Fatigue Failure of Hydraulic Power Equipment during a Long Service Life</atitle><jtitle>Steel in translation</jtitle><stitle>Steel Transl</stitle><date>2023-03-01</date><risdate>2023</risdate><volume>53</volume><issue>3</issue><spage>243</spage><epage>247</epage><pages>243-247</pages><issn>0967-0912</issn><eissn>1935-0988</eissn><abstract>The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of operation and extending the service life of equipment is discussed.</abstract><cop>Moscow</cop><pub>Pleiades Publishing</pub><doi>10.3103/S0967091223030142</doi><tpages>5</tpages></addata></record>
fulltext fulltext
identifier ISSN: 0967-0912
ispartof Steel in translation, 2023-03, Vol.53 (3), p.243-247
issn 0967-0912
1935-0988
language eng
recordid cdi_proquest_journals_2828400051
source SpringerLink Journals - AutoHoldings
subjects Chemistry and Materials Science
Fatigue failure
Fracture mechanics
Hydraulic turbines
Materials Science
Service life
title Fatigue Failure of Hydraulic Power Equipment during a Long Service Life
url https://sfx.bib-bvb.de/sfx_tum?ctx_ver=Z39.88-2004&ctx_enc=info:ofi/enc:UTF-8&ctx_tim=2025-02-03T09%3A04%3A42IST&url_ver=Z39.88-2004&url_ctx_fmt=infofi/fmt:kev:mtx:ctx&rfr_id=info:sid/primo.exlibrisgroup.com:primo3-Article-proquest_cross&rft_val_fmt=info:ofi/fmt:kev:mtx:journal&rft.genre=article&rft.atitle=Fatigue%20Failure%20of%20Hydraulic%20Power%20Equipment%20during%20a%20Long%20Service%20Life&rft.jtitle=Steel%20in%20translation&rft.au=Rudenko,%20A.%20L.&rft.date=2023-03-01&rft.volume=53&rft.issue=3&rft.spage=243&rft.epage=247&rft.pages=243-247&rft.issn=0967-0912&rft.eissn=1935-0988&rft_id=info:doi/10.3103/S0967091223030142&rft_dat=%3Cproquest_cross%3E2828400051%3C/proquest_cross%3E%3Curl%3E%3C/url%3E&disable_directlink=true&sfx.directlink=off&sfx.report_link=0&rft_id=info:oai/&rft_pqid=2828400051&rft_id=info:pmid/&rfr_iscdi=true