Fatigue Failure of Hydraulic Power Equipment during a Long Service Life

The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Steel in translation 2023-03, Vol.53 (3), p.243-247
Hauptverfasser:	Rudenko, A. L., Mishakin, V. V., Fomin, A. E., Sergeeva, O. A.
Format:	Artikel
Sprache:	eng
Schlagworte:	Chemistry and Materials Science Fatigue failure Fracture mechanics Hydraulic turbines Materials Science Service life
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Beschreibung
Zusammenfassung:	The fatigue failure problem of parts of a hydraulic turbine after a long service life is considered. State analysis of elements of hydraulic power equipment and a method for assessing the residual resource of a part in the presence of cracking are presented. The assessment problem of reliability of operation and extending the service life of equipment is discussed.
ISSN:	0967-0912 1935-0988
DOI:	10.3103/S0967091223030142