Influence of composition ratio on structural, optical and magnetic properties of NiFe2O4/(1−x)MnO−xCoO composites

NiFe 2 O 4 and NiFe 2 O 4 /[(1− x )MnO− x CoO] ( x  = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1) samples were produced utilizing co-precipitation procedure. The possibility of formed samples with a single phase or nanocomposite in NiFe 2 O 4 /[(1− x )MnO− x CoO] system was studied using search match progra...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of materials science. Materials in electronics 2022-10, Vol.33 (30), p.23555-23565
Hauptverfasser: Heiba, Zein K., Mohamed, Mohamed Bakr, Abd Ellatief, Ah, El-naggar, A. M., Badawi, Ali
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:NiFe 2 O 4 and NiFe 2 O 4 /[(1− x )MnO− x CoO] ( x  = 0.0, 0.1, 0.3, 0.5, 0.7, 0.9 and 1) samples were produced utilizing co-precipitation procedure. The possibility of formed samples with a single phase or nanocomposite in NiFe 2 O 4 /[(1− x )MnO− x CoO] system was studied using search match program X’Pert HighScore Plus. The structural and microstructural parameters of each sample were obtained applying Rietveld analysis. The compositions and morphologies of the samples were explored using Energy-dispersive X-ray analysis, scanning electron microscope images and transmission electron microscope techniques. The linear and nonlinear optical characteristics of the samples with different composition ( x ) were investigated using UV–vis diffuse reflectance spectra. The optical bandgap value of NiFe 2 O 4 (NFO) reduced regularly from 1.59 to 1.43 eV in the sample with x  = 0.1 (single phase structure). In the samples with the composite structures, the optical band gap reduced irregularly attained its lowest value (1.13 eV) for the sample with x  = 0.9. NFO showed superparamagnetic nature while other samples displayed good ferromagnetic characteristics. The saturation magnetization values for pure NFO and samples with x  = 0.0, 0.5 and 1.0 are 38.1, 29.7, 26.81 and 22.34 emu/gm, respectively. The remanence (M r ) and magnetic squareness (M r /M s ) values of NFO (3.47 emu/g, 0.09) were reduced to (0.55 emu/g, 0.02) upon doping with Mn ions only, while both enhanced to (7.13 emu/g, 0.27) when Co 3 O 4 entered the matrix. The coercivity was decreased when NFO doped with Mn only, while it increased as Co 3 O 4 existed in addition to the Mn ions.
ISSN:0957-4522
1573-482X
DOI:10.1007/s10854-022-09115-7