Effects of Er-doping on the Structure and Photoelectric Properties of 0.825K0.5Na0.5NbO3-0.175Sr (Yb0.5Nb0.5) O3 Ceramics

Multifunctional ceramics of 0.825K 0.5 Na 0.5 NbO 3 -0.175Sr(Yb 0.5 Nb 0.5 )O 3 - x %Er with ferroelectric, transparent and luminescent properties were obtained by doping Er. The effects of Er-doping on the structure, luminescence and electrical properties of the ceramics were studied. After Er doping, the ceramics have luminescent properties and the luminescence intensity reaches the maximum when x =0.75. The ceramics still have good light transmission, but the transmittance decreases with the increase of Er-doping content due to the change of phase structure from pseudo-cubic phase to three-phase orthogonality. The energy storage properties is also greatly improved, and the W rec and the η of the ceramics reach the maximum value of 0.31 J/cm 3 and 94.6% when x =0.25, respectively. At the same time, the maximum electro-induced strain value is 0.031%.