Highly Resolved X‐Ray Imaging Enabled by In(I) Doped Perovskite‐Like Cs3Cu2I5 Single Crystal Scintillator

Low‐dimensional perovskite halides have shown a great potential as X‐ray detection materials because of efficient exciton emissions originating from strongly spatially localized charge carriers. Nonetheless, most of them have a scintillation yield far below their theoretical limits. Here, it is found that the harvesting efficiency of produced charge carriers can be significantly enhanced via a small amount of In+ doping in these highly localized structures. A bright and sensitive zero‐dimensional Cs3Cu2I5:In+ halide with efficient and tunable dual emission is reported. The radioluminescence emission of Cs3Cu2I5:In+ crystals under X‐ray excitation consists of a self‐trapped exciton emission at 460 nm and an In+‐related emission at 620 nm at room temperature. In+ doping enhances the photoluminescence quantum efficiency (PLQY) of Cs3Cu2I5 from 68.1% to 88.4%. Benefiting from the higher PLQY, Cs3Cu2I5:In+ can achieve an excellent X‐ray detection limit of 96.2 nGyair s−1, and a superior scintillation yield of 53 000 photons per MeV, which is comparable to commercial CsI:Tl single crystals. As a result, a remarkable X‐ray imaging resolution of 18 line pairs mm–1 is demonstrated, which is so far a record resolution for single crystal perovskite‐based flat‐panel detectors. These results highlight the importance of efficient harvesting of carriers (and excitons) in low‐dimensional perovskites for radiation detection applications. A remarkable X‐ray imaging resolution of 18 line pairs mm−1 is demonstrated by using bright and sensitive zero‐dimensional Cs3Cu2I5:In+ single‐crystal scintillators, which is so far a record resolution for single‐crystal perovskite scintillator‐based flat‐panel detectors. The result highlights the importance of efficient harvesting of carriers (and excitons) in low‐dimensional perovskites for efficient radiation detection applications.