Photocatalytic degradation of methyl orange by Ca doped β-In2S3 with varying Ca concentration

Industrial wastewater is becoming a universal environmental problem, wherein toxic organic compounds are important sources of pollution. For the degradation toxic organic compounds, semiconductor-based photocatalysis has attracted wide attentions due to their photo-electric properties and high efficiency. Due to lots of advantages of β -In 2 S 3 and the promotion role of Ca-doped on the photocatalytic performance, the photocatalytic degradation of methyl orange by Ca doped β -In 2 S 3 with varying Ca concentration were investigated. The results showed that calcium ion mainly entered into the crystalline lattices of β -In 2 S 3 and the addition of Ca has changed the band structure of In 2 S 3 . The Ca 0.8 - β -In 2 S 3 had a more abundant lamellar morphology and greater specific surface area than other Ca-doped β -In 2 S 3 . The increase in the adsorption sites and photocatalytic reaction sites, allowing Ca 0.8 - β -In 2 S 3 to show the highest photocatalytic activity, which could degrade 98.37% of Methyl Orange (MO) in just 30 min. The improved photocatalytic performance of Ca 0.8 - β -In 2 S 3 was also owed to the stronger visible light absorption, narrower band gap (2.16 eV), and photogenerated the effective separation of electron–hole pairs (e − /h + ). When the light was shone onto the surface of Ca 0.8 - β -In 2 S 3 , more charge carriers and ·O 2 − were excited because Ca 0.8 - β -In 2 S 3 had a narrower band gap and lower CB position. Additionally, h + played a dominant role on the photocatalytic degradation of MO. Furthermore, the optimized Ca 0.8 - β -In 2 S 3 photocatalyst had excellent stability and recoverability, which would be greatly helpful for practical application. The present work demonstrated that the optimal doping amount of Ca-doped β -In 2 S 3 was 5.8%, which provides a favorable guideline for the further application of Ca-doped β -In 2 S 3 to degrade pollutants.