Chemical Bath Deposited Orthorhombic SnS Films for Solar Cell Applications

Tin sulfide (SnS) thin films were deposited by the chemical bath deposition technique. The used procedure allows us to obtain orthorhombic SnS in 3.5 h and achieve thicknesses of 390 nm. We study the influence of deposition times, percentage of Sn precursor, and post-annealing on the structural and...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Coatings (Basel) 2022-02, Vol.12 (2), p.283
Hauptverfasser: Ocampo-Ortega, Carlos, Riech, Ines, Abelenda, Arturo, Mis-Fernández, Ricardo, Rodríguez-Fragoso, Patricia, Mendoza-Alvarez, Julio
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Tin sulfide (SnS) thin films were deposited by the chemical bath deposition technique. The used procedure allows us to obtain orthorhombic SnS in 3.5 h and achieve thicknesses of 390 nm. We study the influence of deposition times, percentage of Sn precursor, and post-annealing on the structural and optical properties. The X-ray diffraction measurements of SnS films prepared at a deposition time of 3 h showed orthorhombic structure with characteristic peaks of SnS2. However, increasing the deposition time and the Sn precursor, the orthorhombic SnS phase in these samples becomes predominant. Thin-film morphologies and thicknesses were identified by scanning electron microscopy (SEM). An increase in bandgap from 1.41 eV to 1.56 eV was observed by increasing Sn precursor. The optical properties remain constant after air annealing of 285 °C. Low-temperature photoluminescence spectra show emission bands at 2.5 eV attributed to the presence of SO2. Other deep level transitions were observed at about 0.9 eV, probably due to oxygen.
ISSN:2079-6412
2079-6412
DOI:10.3390/coatings12020283