Reasonable design of a V2O5-x/TiO2 active interface structure with high polysulfide adsorption energy for advanced lithium-sulfur batteries

A sulfur composite active material for lithium-sulfur batteries with a highly active interface structure can display excellent electrochemical performances. For this reason, in this paper, we design a type of V2O5-x/TiO2 active interface structure with high polysulfide adsorption energy as a high-pe...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Electrochimica acta 2022-01, Vol.403, p.139723, Article 139723
Hauptverfasser: Lang, Xiaoshi, Wang, Tan, Wang, Zhenhua, Li, Lan, Yao, Chuangang, Cai, Kedi
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:A sulfur composite active material for lithium-sulfur batteries with a highly active interface structure can display excellent electrochemical performances. For this reason, in this paper, we design a type of V2O5-x/TiO2 active interface structure with high polysulfide adsorption energy as a high-performance sulfur-wrapped matrix. Physical property characterization indicates this interface is constructed from circular anatase structure TiO2 and anoxic vanadium oxide structure composed of V4+ and V5+. After sulfur wrapping, Ti-S and S-S bond structures are produced by chemical and physical adsorption. Density functional theory calculations show that the V2O5-x/TiO2 interface has very high adsorption energy (-5.93 eV) with lithium polysulfide (Li2S6). After sulfur wrapping as a cathode active material, it displays low electrochemical charge transfer resistance (31.89 Ω) and high lithium-ion transfer efficiency (3.50 × 10−12). In addition, it has rather high discharge specific capacities of 1466.47, 963.84 and 801.16 mAh.g−1 at 0.1, 0.2 and 0.5 C, respectively. After 500 cycles, the discharge capacity retention at 0.5 C is up to 76.11% corresponding to 0.048% capacity decay rate per cycle. This is the reason that the V2O5-x/TiO2 active interface has very strong adsorption to polysulfide and can effectively suppress the shuttle effect (Qlow/Qhigh=1.44 at 0.2 C).
ISSN:0013-4686
1873-3859
DOI:10.1016/j.electacta.2021.139723