Spontaneous inversion of the submicron ceramic layer deposited on steel and the copper droplet positioned on their top (case of ceramic poorly wetted by liquid Cu)

In this paper, 50 … 680 nm thick AlN-Al 2 O 3 coatings are deposited by magnetron sputtering on the surface of a steel substrate and a piece of copper is melted on top of the ceramic. Upon heating the ceramic layer is cracked, and the phase inversion of the two top phases from steel/ceramic/copper configuration to the steel/copper/ceramic configuration takes place within 30 s of liquid time of copper. This phase inversion process is accompanied by a Gibbs energy change of about − 1.78 J/m 2 , due to good wettability of solid deoxidized steel by liquid copper in contrary to poor wettability of the ceramic by the copper. When copper is melted on AlN-Al 2 O 3 coating with its thicknesses smaller than a critical value of about 170 ± 60 nm, liquid copper droplets hanging down into the cracks within the ceramic reach the solid steel surface at the bottom of the cracks, thus the flow of Cu down along the cracks is enabled. However, when copper is melted on AlN-Al 2 O 3 with its thickness larger than the critical value of 170 ± 60 nm, Cu first forms a non-wetting droplet on top of the ceramics, and only after a certain incubation time it starts flowing down the cracks. This incubation time was found to depend linearly on the thickness of the ceramic, as cracks are filled from the bottom upwards by liquid copper via the evaporation–condensation mechanism. By the end of the process, the steel/copper/ceramic configuration is further stabilized by gravity. Graphical abstract