Durability of Sustainable Ceramics Produced by Alkaline Activation of Clay Brick Residue

Alkali-activated materials (AAMs) were produced using residues from the red ceramic industry as a precursor, and sodium hydroxide (NaOH), potassium hydroxide (KOH), and sodium silicate (Na2SiO3) as alkaline activators. The effect of activators and curing conditions on physical-mechanical properties and durability were evaluated. The processing parameters (amount of water and consistency index) and the activation conditions (the activator contents and curing temperature) were defined based on an experimental design getting the flexural rupture module as the response. The durability behavior was evaluated by natural aging, accelerated aging (simulated rain test), exposure to the marine environment (salt fog), and acidic environments (HCl and H2SO4). The results showed that the NaOH- and KOH-activated samples exhibited inferior mechanical behavior than those activated with Na2SiO3. In the durability studies, due to leaching, there was a decrease in mechanical strength when samples are subjected to aggressive exposure conditions. However, the strength values are still higher than the minimum indicated for traditional ceramic applications.