Investigation on the path process of M doped ZnO (M = Gd, Mg) via the sol-gel method from dried gel to stable nanostructure powder

Doping is one of the effective methods to modify the physical properties of ZnO material in order to extend its applications. An investigation on Zn1-xMxO (M = Gd, Mg and x = 0.00, 0.03) nanopowders that have been synthesized by sol-gel method and sintered at 600 °C for 2 hours was reported. The decomposition process of the dried gel system was investigated by thermal gravimetric analysis (TGA) and the nanopowders with different heating temperature were studied using FT-IR spectroscopy. The crystal structure of the nanopowders after sintering at 600 °C was obtained using X-ray diffraction (XRD). The TGA curves of the samples showed the various weight loss regions corresponding to the removal of starting materials and no weight loss was observed in the temperature range of 300 to 800 °C which corresponded to the phase-crystallization step. The FTIR spectra showed that ZnO band was assigned to the stretching frequency at 669 cm-1 while Gd/Mg doped ZnO was at 668 cm-1 and 666 cm-1. From the XRD studies, the crystal structure of the samples indicated single phase ZnO crystalline and confirmed hexagonal wurtzite structure (space group of P63mc).