The influence of high pressure to crystalline and magnetic structure of Ba 2 FeMoO 6

The behavior of the crystalline and magnetic structure of Ba 2 FeMoO 6 compound in a wide pressure range from 0 to 4.7 GPa was studied. The crystal structure of ceramic sample was described in the framework of SG I4/mmm (No 139) and contains less 10% of anti-site defects. The change of tetragonal structure (I4/mmm) was not observed in all measured pressure range. It was shown multidirectional influence of ambient pressure onto the average interionic distances of metal-ligand in oxygen octahedrons of FeO 6 and MoO 6. For tetragonal structure of Ba 2 FeMoO 6 were determined coefficients of the linear and all-round compressibility. The influence of ambient pressure on the value of magnetic moment of iron sublattice was shown.