Structural and Optical Properties of Boron Doped Cadmium Oxide

Thin films of transparent and conductive CdO and B1,3)w% doped cadmium oxide (CdO: B) (1 and 3) wt %, have been deposited using chemical spray pyrolysis (CSP)) technique on glass substrate temperature of 300°C. Microstructural analysis indicates that X-ray diffraction study shows that the obtained films were polycrystalline. The preferred orientation was along the direction (200) and that the average crystallite size increases with the increasing B content. Morphological properties were studied, by scanning electron microscope (SEM) and atomic force microscopy (AFM) which reveals that the grains have a similar column shape. UV-visible transmission spectroscopy reveal that the prepared thin films are transparent in the visible range, The value of the optical band gap obtained shows a slight increase in its values from 2.43 eV to 2.45 eV as B concentration increasing.