Modelling of mechanical properties of Pa6 based reinforced graphite and graphite nano platelets composites using different aspect ratio

PurposeThis study aims to fabricate and study the effect of five cumulative graphite (G) and graphite nanoplatelets (GNP) filler loading composites by polymerising PA6 precursor; monomer epsilon caprolactam with the two carbons in situ while taking cognisance of the mixing effects (simultaneous stir...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of Engineering, Design and Technology Design and Technology, 2021-06, Vol.19 (4), p.809-827
Hauptverfasser: Umar, Muneer, Ofem, Michael Ikpi, Anwar, Auwal Sani, Salisu, Abubakar Garba
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:PurposeThis study aims to fabricate and study the effect of five cumulative graphite (G) and graphite nanoplatelets (GNP) filler loading composites by polymerising PA6 precursor; monomer epsilon caprolactam with the two carbons in situ while taking cognisance of the mixing effects (simultaneous stirring and sonication at varying amplitudes and duration). Different aspect ratios will be used to model the two streams of polymerisations.Design/methodology/approachHigh viscosity extrusion grade PA6 and synthetic G of less than 2 µm particle size were used as fillers. GNP and G are dried for 6 h in vacuum oven at 90°C. Prior to in situ polymerisation, probe sonication was applied to disperse fillers in molten ɛ-caprolactam, the PA6 monomer. Five carbon loadings were made, that is 5–25 Wt.% for G and 0.5–2.5 Wt.% for GNP composites. Two different sonification regimes were applied 20% sonication amplitude for 20 min (20/20) and 40% sonication amplitude for 10 min (40/10).FindingsBetter tensile properties were achieved using the 20/20 processing streams for both G and GNP. The G- and the GNP-based composites systems of the 20/20 processing stream had tensile modulus and yield strength retained or improved above the unfilled PA6 value. The highest modulus obtained in the 20/20 streams are 1,878 and 1,201 MPa, respectively, for GNP and G at the highest loading levels, while the 40/10 processing streams had 963 and 1,247 MPa, respectively, for the GNP and G.Originality/valueTo the best of the authors’ knowledge, nobody has ever used sonification amplitude to compare mechanical properties.
ISSN:1726-0531
1758-8901
DOI:10.1108/JEDT-04-2020-0112