Selective laser melted near-beta titanium alloy Ti-5Al-5Mo-5V-1Cr-1Fe: Microstructure and mechanical properties

In this work, a near-beta Ti-5Al-5Mo-5V-1Cr-1Fe titanium alloy was fabricated by selective laser melting (SLM), and the microstructure evolution together with the mechanical properties was studied. The as-fabricated alloy showed columnar β grains spreading over multiple layers and paralleling to the building direction. The distinct microstructure of as-fabricated alloy was composed of near- β (more than 98.1 %) with a submicron cellular structure. Different SLM processing parameters such as hatch spacing could affect the microstructure of as-fabricated alloy, which could thus further significantly affect the mechanical properties of as-fabricated alloy. In addition, the as-fabricated alloy with the distinct microstructure exhibits yield strength of 818 MPa combined with elongation of more than 19 %, which shows that SLM is a potential technology for manufacturing near-beta titanium components.