Achieving superior performance in thermoelectric Bi0.4Sb1.6Te3.72 by enhancing texture and inducing high-density line defects

Miniaturization of efficient thermoelectric (TE) devices has long been hindered by the weak mechanical strength and insufficient heat-to-electricity conversion efficiency of zone-melted (ZM) ingots. Here, we successfully prepared a robust high-performance p-type Bi 0.4 Sb 1.6 Te 3.72 bulk alloy by c...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Science China materials 2021-06, Vol.64 (6), p.1507-1520
Hauptverfasser: Qiu, Junhao, Yan, Yonggao, Xie, Hongyao, Luo, Tingting, Xia, Fanjie, Yao, Lei, Zhang, Min, Zhu, Ting, Tan, Gangjian, Su, Xianli, Wu, Jinsong, Uher, Ctirad, Jiang, Hongyi, Tang, Xinfeng
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Miniaturization of efficient thermoelectric (TE) devices has long been hindered by the weak mechanical strength and insufficient heat-to-electricity conversion efficiency of zone-melted (ZM) ingots. Here, we successfully prepared a robust high-performance p-type Bi 0.4 Sb 1.6 Te 3.72 bulk alloy by combining an ultrafast thermal explosion reaction with the spark plasma sintering (TER-SPS) process. It is observed that the introduced excess Te not only enhances the (00 l )-oriented texture to ensure an outstanding power factor (PF) of 5 mW m −1 K −2 , but also induces extremely high-density line defects of up to 10 11 –10 12 cm −2 . Benefiting from such heavily dense line defects, the enhancement of the electronic thermal conductance from the increased electron mobility is fully compensated by the stronger phonon scattering, leading to an evident net reduction in total thermal conductivity. As a result, a superior ZT value of ~1.4 at 350 K is achieved, which is 40% higher than that of commercial ZM ingots. Moreover, owing to the strengthening of grain refinement and high-density line defects, the mechanical compressive stress reaches up to 94 MPa, which is 154% more than that of commercial single crystals. This research presents an effective strategy for the collaborative optimization of the texture, TE performance, and mechanical strength of Bi 2 Te 3 -based materials. As such, the present study contributes significantly to the future commercial development of miniature TE devices.