Polishing single-crystal silicon carbide with porous structure diamond and graphene-TiO2 slurries

In this study, a self-modified diamond (SMD) slurry for mechanical polishing is presented as well as a novel TiO 2 -graphene slurry used with the aid of UV light for a chemical mechanical polishing (CMP) technique that improves the rate of polishing. The surface characteristics and removal rate of s...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:International journal of advanced manufacturing technology 2019-11, Vol.105 (1-4), p.1519-1530
Hauptverfasser: Tsai, Ming Yi, Hoo, Zuan Tang
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In this study, a self-modified diamond (SMD) slurry for mechanical polishing is presented as well as a novel TiO 2 -graphene slurry used with the aid of UV light for a chemical mechanical polishing (CMP) technique that improves the rate of polishing. The surface characteristics and removal rate of silicon carbide (SiC) samples polished with the slurry were compared with the results obtained by polishing with both a conventional diamond slurry and CMP slurry. The experimental results indicated that the material removal rate (MRR) of SiC from the wafer surface with the SMD slurry was higher, and surface finish and lapping efficiency was better than that achievable with other slurries. The experimental data also showed that a TiO 2 -graphene slurry had a higher removal rate compared to the TiO 2 slurry using the same intensity of UV light. The TiO 2 -graphene slurry showed a 3-fold increase in removal rate over that of a traditional CMP slurry. An experiment was also carried out where nanodiamond (50 nm and 500 nm) abrasive was added to the graphene-TiO 2 . As expected, the removal rate increased but the average surface roughness was poor because the nanodiamond particles caused small scratches. The graphene-TiO 2 with nanodiamond abrasives has 5 times the removal rate achieved with a traditional CMP slurry. This novel method can facilitate the extensive production of well-polished single-crystal SiC wafers.
ISSN:0268-3768
1433-3015
DOI:10.1007/s00170-019-04223-x