Phase transition-induced improvement in the capacity of fluorine-substituted LiFeBO3 as a cathode material for lithium ion batteries
Among polyanion-type cathode materials used for large-scale lithium-ion batteries (LIBs), LiFeBO3 (LFeB) has received attention due to its lowest weight framework with a larger theoretical capacity of 220 mAh g−1 compared with commercialized LiFePO4 (170 mAh g−1). The main drawback of LFeB, however,...
Gespeichert in:
Veröffentlicht in: | Electrochimica acta 2021-01, Vol.367, p.137364, Article 137364 |
---|---|
Hauptverfasser: | , , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Among polyanion-type cathode materials used for large-scale lithium-ion batteries (LIBs), LiFeBO3 (LFeB) has received attention due to its lowest weight framework with a larger theoretical capacity of 220 mAh g−1 compared with commercialized LiFePO4 (170 mAh g−1). The main drawback of LFeB, however, is its poor specific discharge capacity as a cathode material for LIBs. Herein, the fluorine-substituted LFeB at the oxygen site, LiFeBO3-xF2x (LFeBF, x = 0.05, 0.1, 0.2, 0.3, and 0.5), has been prepared as a cathode material for LIBs via a solid-state reaction to improve the electrochemical behavior accompanied by phase transition. Morphological change as increasing x and well-distributed fluorine element of LFeBF have been observed using a scanning electron microscope combined with an energy dispersive X-ray spectrometer. X-ray diffraction, X-ray photoelectron spectroscopy, and solid-state 7Li and 11B nuclear magnetic resonance spectroscopy studies of LFeBF as well as increasing x show a dramatic phase transition from monoclinic to vonsenite-type structure. The plausible atomic arrangement has been also investigated using density functional theory. Furthermore, the fluorine substitution at the oxygen site of LFeB leads to a remarkable improvement in discharge capacity, the highest value (361.15 mAh g−1 for LFeBF (x = 0.3)) of which is about five times larger than that of LFeB (73.43 mAh g−1) at 0.05 C rate, without any additional carbon source. |
---|---|
ISSN: | 0013-4686 1873-3859 |
DOI: | 10.1016/j.electacta.2020.137364 |