Effect of Pin Length and Rotation Speed on the Microstructure and Mechanical Properties of Friction Stir Welded Lap Joints of AZ31B-H24 Mg Alloy and AA6061-T6 Al Alloy

In the present work, friction stir welding of 3-mm-thick AA6061-T6 Al alloy and AZ31B-H24 Mg alloy sheets was carried out in lap configuration with Al alloy on top. Experiments were carried out by varying the pin length (3.25, 3.75, and 4.25 mm) and tool rotation speed (600, 800, and 1000 RPM). Micr...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Metallurgical and materials transactions. A, Physical metallurgy and materials science Physical metallurgy and materials science, 2020-12, Vol.51 (12), p.6269-6282
Hauptverfasser: Bandi, Anil, Bakshi, Srinivasa R.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:In the present work, friction stir welding of 3-mm-thick AA6061-T6 Al alloy and AZ31B-H24 Mg alloy sheets was carried out in lap configuration with Al alloy on top. Experiments were carried out by varying the pin length (3.25, 3.75, and 4.25 mm) and tool rotation speed (600, 800, and 1000 RPM). Microstructures of the joint cross-section revealed the presence of a compound intermetallic layer along the interface consisting of Al-rich (Al 3 Mg 2 ) intermetallic compound near the Al alloy side, and Mg-rich intermetallic compound (Mg 17 Al 12 ) near the Mg alloy side. The formation of a eutectic mixture of Mg solid solution and Mg 17 Al 12 was observed at the hook on either side. Two modes of failure were observed; Mode 1 through the interface and Mode 2 due to failure of the sheet. The Mode 1 failure strengths obtained were the highest (148 ± 6 N/mm) compared to the literature and were obtained for the 3.25 and 3.75 mm pin at 800 RPM. A lap shear strength of 212 ± 6 N/mm was obtained with 4.25 mm pin length at 600 RPM, which is the highest reported so far and was attributed to Mode 2 failure. The effect of interface pull-up, angle of the interface at the advancing side, and distribution of intermetallic compounds on the lap-shear strength are discussed.
ISSN:1073-5623
1543-1940
DOI:10.1007/s11661-020-06020-8