Local Fracture of Nanolaminates: Edge Chipping Test

The fracture resistance of domestic and foreign nanolaminate ceramics was studied by the EF (edge fracture) method. This method provides for indentor chipping of rectangular specimen edges, which permits evaluating such fracture resistance characteristics, as chipping resistance and edge toughness. There is no way of experimental determining the stress intensity factor effected as the penetration of a Vickers indentor into the polished specimen surface and measurement of crack sizes that are formed near the angles of its imprint. The influence of stress concentrations in the indentor–specimen surface contact zone on the fracture resistance of ceramics was assessed. Different test stress concentrations were produced with conical diamond indentors of different tip radii. Studies on domestic titanoaluminous carbide Ti 3 AlC 2 specimens demonstrated that with a reduction in stress concentration levels (indentors with increasingly larger tip radii), its edge toughness grew to a smaller extent than that of Y 2 O 3 and TS Mg-PSZ ceramics. It is indicative of the limited sensitivity of an examined material to stress concentrations on local fracture. The ratio of edge toughness determined with the indentors of maximum and minimum tip radii (in this case, 400 and 11 μ m) can serve as a measure of its sensitivity (in comparison to this characteristic for examined materials). Note that the edge toughness of Ti 3 AlC 2 ceramics is almost one-third as large than, e.g., that of Y 2 O 3 ceramics and 1.6 times smaller than that of TS nonlinearly elastic zirconia Mg-PSZ.