Effect of Mg Contents on Catalytic Activity and Coke Formation of Mesoporous Ni/Mg-Aluminate Spinel Catalyst for Steam Methane Reforming

Ni catalysts are most suitable for a steam methane reforming (SMR) reaction considering the activity and the cost, although coke formation remains the main problem. Here, Ni-based spinel catalysts with various Mg contents were developed through the synthesis of mesoporous Mg-aluminate supports by ev...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Catalysts 2020-08, Vol.10 (8), p.828
Hauptverfasser: Kim, Hyunjoung, Lee, Young-Hee, Lee, Hongjin, Seo, Jeong-Cheol, Lee, Kyubock
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:Ni catalysts are most suitable for a steam methane reforming (SMR) reaction considering the activity and the cost, although coke formation remains the main problem. Here, Ni-based spinel catalysts with various Mg contents were developed through the synthesis of mesoporous Mg-aluminate supports by evaporation-induced self-assembly followed by Ni loading via incipient wetness impregnation. The mesoporous Ni/Mg-aluminate spinel catalysts showed high coke resistance under accelerated reaction conditions (0.0014 gcoke/gcat·h for Ni/Mg30, 0.0050 gcoke/gcat·h for a commercial catalyst). The coke resistance of the developed catalyst showed a clear trend: the higher the Mg content, the lower the coke deposition. The Ni catalysts with the lower Mg content showed a higher surface area and smaller Ni particle size, which originated from the difference of the sintering resistance and the exsolution of Ni particles. Despite these advantageous attributes of Ni catalysts, the coke resistance was higher for the catalysts with the higher Mg content while the catalytic activity was dependent on the reaction conditions. This reveals that the enhanced basicity of the catalyst could be the major parameter for the reduction of coke deposition in the SMR reaction.
ISSN:2073-4344
2073-4344
DOI:10.3390/catal10080828