Photocatalytic Degradation of Methylene Blue Using Zinc Oxide/Styrene Butadiene Rubber Photocatalyst

Photocatalytic Degradation of Methylene Blue Using Zinc Oxide/Styrene Butadiene Rubber Photocatalyst

The zinc oxide/styrene butadiene rubber (ZnO/SBR) photocatalyst was successfully prepared via mechanical mixing at 30 °C. ZnO/SBR square shaped (3 x 3 cm) with 0.54 mm thickness was investigated towards photocatalytic degradation of methylene blue (MB) solution under visible light irradiation and co...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Materials science forum 2020-05, Vol.990, p.173-176
Hauptverfasser: Zakaria, Muhammad Salihin, Ishak, Zainal Arifin Mohd, Nordin, Razif, Yusof, Rizana, Wan Ismail, Wan Izhan Nawawi, Latiff, Nadia
Format: Artikel
Sprache:eng
Schlagworte:
Absorption spectra
Butadiene
Light irradiation
Methylene blue
Photocatalysis
Photocatalysts
Photodegradation
Rubber
Styrenes
Zinc oxide
Zinc oxides
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The zinc oxide/styrene butadiene rubber (ZnO/SBR) photocatalyst was successfully prepared via mechanical mixing at 30 °C. ZnO/SBR square shaped (3 x 3 cm) with 0.54 mm thickness was investigated towards photocatalytic degradation of methylene blue (MB) solution under visible light irradiation and compared with bare ZnO and raw SBR. FTIR absorption spectra reveal the characteristic peaks and estimated intensity of conjugated carbon for ZnO/SBR. ZnO/SBR showed excellent photocatalytic performance nearly as good as bare ZnO.
ISSN:0255-5476
1662-9752
1662-9752
DOI:10.4028/www.scientific.net/MSF.990.173