Thermomechanical treatments influence on the phase composition, microstructure, and selected mechanical properties of Ti–20Zr–Mo alloys system for biomedical applications

The study and development of new titanium alloys aim to place a metallic biomedical device with better mechanical compatibility with the bone, that is, with a smaller Young's modulus, on the market, to improve its application in the orthopedic and dental fields. This study analyzed the influenc...

Ausführliche Beschreibung

Gespeichert in:
Bibliographische Detailangaben
Veröffentlicht in:Journal of alloys and compounds 2020-01, Vol.812, p.152108, Article 152108
Hauptverfasser: Kuroda, P.A.B., Lourenço, M.L., Correa, D.R.N., Grandini, C.R.
Format: Artikel
Sprache:eng
Schlagworte:
Online-Zugang:Volltext
Tags: Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
Beschreibung
Zusammenfassung:The study and development of new titanium alloys aim to place a metallic biomedical device with better mechanical compatibility with the bone, that is, with a smaller Young's modulus, on the market, to improve its application in the orthopedic and dental fields. This study analyzed the influence of thermomechanical treatments on the structure, hardness, and elastic modulus of the Ti–20Zr–Mo ternary alloy system, where the molybdenum content varied between 0 and 10 wt%. The treatments performed in this study involved homogenization, hot-rolling, and annealing. The structural and microstructural analyses were performed by X-ray diffraction, optical and scanning electron microscopy. An analysis of the mechanical properties of the alloy was obtained by measuring Vickers microhardness and the dynamic elastic modulus. The structural and microstructural results indicated that the Ti–20Zr alloy has only the α′ phase, the Ti–20Zr–10Mo alloy had a predominance of β phase, and the other alloys were α+β types. The hardness increased due to solid-state hardening with the increase of the molybdenum content and due to hot-rolling processing, which increased the internal stresses of the material. The elastic modulus decreased with higher levels of molybdenum and the hot-rolling processing, due to β phase stabilization. The other treatments increased the elastic modulus and may even induce the formation of the omega phase in some alloys of the system. •Ti–20Zr–Mo alloys exhibited the coexistence of α” and β phases.•Crystalline structure and phase proportion of Ti–20Zr–Mo alloys were sensitive to the chemical composition and thermomechanical treatments.•Thermomechanical treatments of Ti–20Zr–Mo alloys led to variations in the Vickers microhardness and Young's modulus values.