Post‐Treatment of CH3NH3PbI3/PbI2 Composite Films with Methylamine to Realize High‐Performance Photoconductor Devices
Organometallic halide perovskites have attracted great research interest as light‐active materials for use in optoelectronics. Here, we report a high‐performance photoconductor based on a methylammonium lead iodide (MAPbI3) film that was prepared from a methylamine‐treated MAPbI3/PbI2 perovskite fil...
Gespeichert in:
Veröffentlicht in: | Chemistry, an Asian journal an Asian journal, 2019-08, Vol.14 (16), p.2861-2868 |
---|---|
Hauptverfasser: | , , , , , , , , , |
Format: | Artikel |
Sprache: | eng |
Schlagworte: | |
Online-Zugang: | Volltext |
Tags: |
Tag hinzufügen
Keine Tags, Fügen Sie den ersten Tag hinzu!
|
Zusammenfassung: | Organometallic halide perovskites have attracted great research interest as light‐active materials for use in optoelectronics. Here, we report a high‐performance photoconductor based on a methylammonium lead iodide (MAPbI3) film that was prepared from a methylamine‐treated MAPbI3/PbI2 perovskite film. An ultrahigh responsivity of 3.6 A W−1 and detectivity of 5.4×1012 Jones were obtained for the film under 0.5 mW cm−2 white‐light illumination. In addition, under 420 nm light irradiation, the film exhibited its highest responsivity and detectivity of 30 A W−1 and 2.4×1014 Jones, respectively. The excellent photo‐response performance results from the improved electronic quality and suppressed nonradiative recombination channels of the treated perovskite thin film.
Caught on film: A high‐performance photoconductor based on CH3NH3PbI3 film prepared from methylamine‐treated CH3NH3PbI3/PbI2 perovskite films is reported. |
---|---|
ISSN: | 1861-4728 1861-471X |
DOI: | 10.1002/asia.201900644 |