Influence of the melamine content in melamine-urea-formaldehyde resins on formaldehyde emission and cured resin structure

The effect of melamine content in melamine-urea-formaldehyde (MUF) resins on the formaldehyde emission and resin structure was investigated using six MUF resins synthesized with different F/(M + U) and M/U molar ratios. The formaldehyde emission from the plywood decreased-as the F/(M + U) molar ratio decreased and the M/ U molar ratio increased. In addition, the bond performance was enhanced as the M/U molar ratio increased in the MUF resins with a fixed F/(M + U) molar ratio. Quantitative solution sup13 C-NMR spectra of MUF resins revealed that the MUF resins with a high melamine content consisted of more highly branched crosslinkage structure and free melamine compared to the resins with low melamine con-tents. Furthermore, solid-state sup13 C CP-MAS NMR spectra of cured MUF resins proved that more methylol groups, dimethylene ether, and branched methylene structures were present in the MUF resins with a higher F/(M + U) molar ratio, leading to increased bond strength and formaldehyde emission. There is no significant difference in the linkage structure of the cured resins with the same F/(M + U) and different M/U molar ratios except the ratios of carbonyl carbon of urea and triazine carbon of melamine. Therefore, the lower formaldehyde emission from cured MUF resins with a higher M/U molar ratio might be ascribed to the stronger linkages between triazine carbons of