Photoluminescence and scintillation properties of Eu-doped TeO2-Al2O3-BaO glasses

We synthesized TeO 2 -Al 2 O 3- BaO glasses with different concentrations of Eu (0, 0.1, 0.5, 1.0 and 5.0 mol%) by the conventional melt-quenching technique to develop scintillator materials. After the synthesis, photoluminescence (PL) and scintillation properties of the samples were investigated systematically. The Eu-doped samples exhibited emissions with peaks approximately at 590 and 620 nm due to the 4f-4f transitions of Eu 3+ in PL and scintillation. Among the sample investigated, the 5.0% Eu-doped sample showed the highest PL and scintillation intensities. In addition, decay time constants of the Eu-doped samples in PL and scintillation were about 0.91–0.94 and 0.37–0.51 ms, respectively. Furthermore, the afterglow levels of the samples were estimated to be 179–245 ppm, which was approximately one order of magnitude higher than those of Bi 4 Ge 3 O 12 and CdWO 4 .