•Category D of the Aluminum Design Manual is recommended for fatigue resistance analysis of welded aluminum hand-hole details.•Fatigue test results for the light poles with hand-holes demonstrated that the majority of failures happen in stress ranges larger than 13.8 MPa (2 ksi).•During static testi...

Ausführliche Beschreibung

Gespeichert in:

Bibliographische Detailangaben
Veröffentlicht in:	Engineering structures 2019-06, Vol.188, p.60-68
Hauptverfasser:	Daneshkhah, Ali Reza, Schlatter, Clark R., Rusnak, Cameron R., Menzemer, Craig C.
Format:	Artikel
Sprache:	eng
Schlagworte:	Aluminum Bending fatigue Category D of Aluminum Design Manual Crack propagation Cyclic loads Design Design S-N curve Fatigue cracking Fatigue failure Fatigue life Fatigue test Fatigue tests Finite element method Fracture mechanics High cycle fatigue Luminaires Reinforcement rings S N diagrams Static test Utility poles Welded aluminum hand-hole details Welding Wiring
Online-Zugang:	Volltext
Tags:	Tag hinzufügen Keine Tags, Fügen Sie den ersten Tag hinzu!

Schreiben Sie den ersten Kommentar!