Effect of L-Cysteine on Photoluminescence of Zns:F Quantum Dots

ZnS:F quantum dots (QDs) capping with and without L-cys were synthesized by a solid-state method at low temperature, and the influence of L-cys on the properties of ZnS:F QDs were investigated. The crystal structure, surface morphology and luminescent properties of the samples were analyzed by X-ray diffractometer (XRD), transmission electron microscope (TEM), fourier transform infrared (FTIR), photoluminescence spectrometer (PL) and ultraviolet-visible spectrometer (UV-Vis). The results showed that all samples had a zinc blende structure with particle size in the range of 2-6 nm. The emission intensity was significantly enhanced after capping with L-cys, and the strongest luminescence was obtained when the ratio of L-cys/ZnS:F was 0.8:1, and was about 2.5 times of that of ZnS:F QDs. The capping of L-cys increased the grain size of ZnS:F QDs and their water solubility.