Effect of electrochemical control function on the internal structure and composition of electrodeposited polypyrrole films: A neutron reflectometry study

Electrodeposited conducting polymer films derived from aromatic monomers are known to possess properties that depend significantly on the deposition protocol, particularly the electrochemical control function employed. This study explores the underlying reasons for this common observation for the specific case of polypyrrole films deposited from aqueous media onto gold electrodes under potentiostatic, potentiodynamic and galvanostatic control. Although the control functions impose different conditions, the control parameters (potential, potential range and scan rate, and current) were selected so as generate films at comparable rates; this avoids inappropriate attribution of structural and compositional variations to different thickness regimes, irrespective of how they were generated. In each case, film deposition was periodically interrupted and the film characterised by specular neutron reflectivity measurements. By using d4-pyrrole monomer in H2O solvent, the isotopic selectivity of neutron reflectivity was used to extract polymer and solvent concentration profiles as a function of distance from the electrode/film interface. Spatial integration of these profiles was used to quantify total film solvent populations; these are expressed as solvent volume fractions. Films grown under the three different control regimes have measurably distinct solvent volume fraction profiles and there is evolution of these profiles with increasing thickness. Ultimately, for the conditions employed, the order of increasing porosity (i.e. solvent content) by control function was potentiostatic